HDPE Geomembrane Surface: Smooth or Textured Feature: Puncture Resistance, Impact Resistance, Tear Resistance Color: Black Thickness: 0.5- 3 Mm Length: as Per Customer Request Trademark: RUNTONG Origin: Dezhou, China Certification: ISO Application: Transportation Project, Hydraulic Project, Geotechnical Project, Environmental Project Material: HDPE Other Material: LDPE, LLDPE, EVA, Ecb, PVC etc Width: 2- 6 M Temperature Condition: -70 to +70 Celsius Degree Specification: ASTM or GB HS Code: 39219090 High density polyethylene HDPE
Geomembrane film sheet roll
Introduction
HDPE geomembrane is made of high density polyethylene resin as a waterproof barrier material production. Geomembrane has excellent resistance to environmental stress cracking resistance, low temperature resistance, aging resistance, corrosion resistance, and large temperature range (-60--+60) and long service life (50 years).
Physical properties
1, Excellent chemical resistance, corrosion resistance
2, The outstanding resistance to stress cracking (ESCR);
3, The lowest permeability;
4, UV resistance, excellent;
5, Embrittlement performance of cold resistance of the stable;
Characteristic
1, HDPE geomembrane is a kind of flexible waterproof material, seepage coefficient is very high
2, HDPE geomembrane has good heat resistance and cold resistance, the use of environmental temperature is 110 ° C high temperature, low temperature -70 ° C;
3, HDPE geomembrane has good chemical stability, corrosion resistance to acid, alkali, oil is good anticorrosive material;
4, HDPE geomembrane has a very high tensile strength, so that it has a very high tensile strength can meet the high standards of the project need;
5, HDPE geomembrane has a strong weather resistance, strong aging resistance performance, can long time exposed to use in th sun and maintain the original properties.
6, HDPE geomembrane has strong tensile strength and elongation at break, make HDPE geomembrane can be used in a variety of adverse geological and climatic conditions. To adapt to the geological uneven settlement and strong strain!
NO | Item | Value |
0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm |
1 | Density (g/cm 2 ) | 0.939 |
2 | Tensile propeties | | | | | | | |
| Yield strength (N/mm) | 11 | 15 | 18 | 22 | 29 | 37 | 44 |
| Break strength (N/mm) | 20 | 27 | 33 | 40 | 53 | 67 | 80 |
| Yield elongation (%) | 12 |
| Break elongation (%) | ≥450 |
3 | Tear resistance (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 |
4 | Puncture resistance (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 |
5 | Stree crack tensistance (h) | ≥1500 |
6 | Carbon black | | | | | | | |
| Carbon black content (%) | 2.0-3.0 |
| Carbon black dispersion | Carbon black dispersion (only near spherical agglomerates)fo r10 different |
| views 9 in categories 1 or 2 and 1 in category3 | |
7 | Oxidative induction time(OIT) | | | | | | | |
| Standard OIT(min) | 100 |
| High pressure OIT(min) | 400 |
8 | Oven aging at 85 °C | | | | | | | |
| Standard OIT-% retained after 90 days (%) | 55 |
| High pressure OIT-% retained after 90 days (%) | 80 |
9 | UV Resistance | | | | | | | |
| Standard OIT retained after 1600 hrs (%) | 50 |
| High pressure OITretained after 1600 hrs (%) | 50 |
10 | Low tempreture impact brittle property at -70 °C | Pass |
11 | Premeability ( g. cm/(cm 2 ). Pa) | ≤ 1.0×10 -13 |
12 | Dimensional stability (%) | ±2 |
Contact us if you need more details on HDPE Sheet. We are ready to answer your questions on packaging, logistics, certification or any other aspects about HDPE Geomembrane、
Pond liner. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Geomembrane Welder